原料技術(shù)數(shù)據(jù)
性能項(xiàng)目 | 試驗(yàn)條件[狀態(tài)] | 測(cè)試方法 | 測(cè)試數(shù)據(jù) | 數(shù)據(jù)單位 | |
物理性能 | 模具收縮率 | 3.2mm | ASTM D-955 | - | E-3 |
比重 | ASTM D-792 | - | |||
吸水率 | ASTM D-570 | - | % | ||
機(jī)械性能 | 沖擊強(qiáng)度缺口 | 23℃ | ASTM D-256 | 535 | J/m |
拉伸強(qiáng)度(屈伏點(diǎn)) | ASTM D-638 | 67 | Mpa | ||
彎曲模量 | ASTM D-790 | 2691 | Mpa | ||
彎曲強(qiáng)度 | ASTM D-790 | 103 | Mpa | ||
拉伸率(斷裂點(diǎn)) | ASTM D-638 | 50 | % | ||
拉伸模量 | ASTM D-638 | - | Mpa | ||
洛氏硬度 | ASTM D-785 | - | R | ||
電氣性能 | 表面電阻 | ASTM D-257 | - | Ohm-cm | |
損耗因數(shù) | 1MHz | ASTM D-150 | - | ||
體積電阻 | ASTM D-257 | - | Ohm-cm | ||
介電常數(shù) | 1MHz | ASTM D-150 | - | ||
熱性能 | 阻燃性 | UL-94 | 1.5 | UL94 | |
熱變形溫度 | 1.8Mpa | ASTM D-648 | 86 | ℃ | |
UL長(zhǎng)期使用溫度 | 無(wú)沖擊 | UL-746B | 75 | ℃ | |
維卡軟化點(diǎn) | ASTM D-525 | - | ℃ | ||
熱變形溫度 | 0.45Mpa | ASTM D-648 | - | ℃ | |
阻燃性 | UL-94 | V-0 | |||
線膨脹系數(shù) | E831 | - | 1/℃ | ||
UL長(zhǎng)期使用溫度 | 含沖擊 | UL-746B | 65 | ℃ |